6061铝合金上硅烷膜的制备与性能
          
Preparation and Properties of Silane Film on 6061 Aluminium Alloy Surface

摘    要
采用浸涂技术, 在6061铝合金表面制备了γ-氨丙基三甲氧基硅烷膜。采用电化学方法和SEM研究了其在3.5% NaCl溶液中的耐蚀性及形貌。结果表明,当硅烷浓度为3%(体积分数), 溶液pH为12, 室温下水解时间72 h形成的硅烷溶液具有较好的稳定性; 铝合金试样在硅烷溶液中浸涂3 min, 固化温度180 ℃, 固化时间120 min, 其表面形成的硅烷膜的耐蚀性最佳, 表现为腐蚀电流密度降低和腐蚀电位的升高。
标    签 铝合金   硅烷膜   极化曲线   耐蚀性   aluminium alloy   silane film   polarization curve   corrosion resistance  
 
Abstract
The γ-aminopropyltriethoxysilane film was deposited on 6061 aluminium alloy surface. The corrosion resistance of the silane film was investigated in 3.5% NaCl solution, using Tafel polarization curves. The results showed that silane solution was stable when the silane concentration was 3%, pH value was 12 and time of hydrolysis was 72 h at room temperature. When aluminum alloy specimen in silane solution was treated by dip-coating 3 min, curing temperature 180 ℃ and curing time 120 min. the obtained silane films on 6061 aluminium alloy surface had the best corrosion resistance, the corrosion current density reduced and corrosion potential rose.

中图分类号 TG174

 
  中国光学期刊网论文下载说明


所属栏目 试验研究

基金项目

收稿日期 2013/3/12

修改稿日期

网络出版日期

作者单位点击查看


备注张圣麟(1960-),教授,博士,从事材料腐蚀与防护研究,

引用该论文: LEI Yue,TANG Hong-Wei,ZHANG Sheng-lin. Preparation and Properties of Silane Film on 6061 Aluminium Alloy Surface[J]. Corrosion & Protection, 2014, 35(1): 64


被引情况:


【1】李文超,张明明,雷 越,乔静飞,张圣麟, "氯化铈掺杂对6061铝合金表面硅烷膜性能的影响",腐蚀与防护 36, 832-835(2015)



论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】王元良,周友龙,胡久富. 铝合金汽车轻量化及其焊接新技术[J]. 现代焊接,2006,7(8):1-4.
 
【2】汪亮,宣天鹏,周贇,等. 铝合金表面新型硅烷膜的制备及表面形貌研究[J]. 电镀与精饰,2012,34(3):13-17.
 
【3】孙宝德,李克. 铝及铝合金防腐蚀表面处理技术的研究现状与发展[J]. 腐蚀与防护,1998,19(5):195-198.
 
【4】闫星宇,白术波,肖围. 纳米SiO2协同稀土铈对旅馆表面硅烷膜的耐蚀性研究[J]. 电镀与环保,2010,30(3):36-40.
 
【5】PALANIVEL V,ZHU D,VAN Ooij W J. Nanoparticle-filled silane films as chromate replacements for aluminium alloys[J]. Prog Org Coat,2003,47:384-392.
 
【6】HINTON B R. Corrosion inhibition with rare earth metal salts[J]. Journal of Alloys and Compounds,1992,180(1):15-19.
 
【7】周丽. LY12 铝合金表面防腐蚀工艺[J]. 腐蚀与防护, 2012,33(9): 810-812.
 
【8】王雪明,李爱菊. 金属表面制备KH-560硅烷膜涂层的工艺研究[J]. 中国表面工程,2004,17(6):27-31.
 
【9】胡会利,陈丽娇. 表面转化膜五铬化技术的研究动向[J]. 腐蚀与防护,2009,30(10):727-731.
 
【10】SUBRAMANIAN V,VAN O W J. Silane based metal pretreatments as alternatives to chromating[J]. Surface Engineering,1999,15(2):1-5.
 
【11】Child T,Van O W J. Application of silane technology to prevent corrosion of metals and improve paint adhesion[J]. Trans IMF,1999,77(2):64-70.
 
【12】吴海江,卢锦堂,陈锦虹. 热镀锌钢板表面硅烷耐蚀性能的初步研究[J]. 腐蚀与防护,2006,27(1):14-17.
 
【13】徐溢,王楠,张小风,等. 直接用作金属表面新型防护涂层的硅烷偶联剂水解效果分析[J]. 腐蚀与防护,2000,21(4):157.
 
【14】CHICO B,GALVAN J C. Electrochemical impedance spectroscopy study of the effect of curing time on the early barrier properties of silane systems applied on steel substrates[J]. Progress in Organic Coating,2007,60:45-53.
 
【15】季献武,时士峰,肖嵘,等. 硅烷处理对涂层/金属体系耐蚀性能的影响[J]. 腐蚀与防护, 2012,33(10): 1081-1086.
 
【16】MONTEMOR M F,FERREIRA M G S. Analytical and microscopic characterization of modified bis-[triethoxysilylpropyl] tetrasulphide silane films on magnesium AZ31 substrates[J]. Progress in Organic Coating,2007,60:228-237.
 
【17】韩丽华,马国庆. 镀锌层表面KH-560硅烷膜耐蚀性能研究[J]. 材料工程,2010,6:45-49.
 
【18】ZHU D Q,WIM J O. Corrosion protection of AA 2024-T3 by bis-[3-(triethoxysilyl)propyl] tetrasulfide in neutral sodiumchloride solution[J]. Corrosion Science,2003,45:2163-2175.
 
【19】周宁琳. 有机硅聚合物导论[M]. 北京:科学出版社,2000.
 
【20】闫斌,陈宏霞,陈嘉宾. 功能性有机硅烷膜对金属腐蚀防护的研究现状及展望[J]. 材料保护,2009,42(3):54-56.
 
【21】吴超云,张津. 金属表面硅烷防护膜层的研究进展[J]. 表面技术,2009,6(38):79-82.
 
相关信息
   标题 相关频次
 氯化铈掺杂对6061铝合金表面硅烷膜性能的影响
 7
 AA6061-T6铝合金表面纳米Y2O3改性硅烷膜的耐蚀性
 6
 氧化钇掺杂对铝合金表面硅烷膜耐蚀性的影响
 6
 冷轧钢表面磷化膜和硅烷膜的制备与性能
 5
 铝合金黑色抗蚀化学氧化膜
 5
 铝合金稀土磷化与铬磷化比较
 5
 稀土氯化物对6061铝合金原位磷化有机涂层耐蚀性的影响
 5
 AM60压铸镁合金表面微弧氧化陶瓷层的耐蚀性电化学分析
 4
 常温铁系磷化工艺研究
 4
 镀锌板的复合钝化
 4
 镀锌板铈钼复合成膜工艺及其耐蚀性能
 4
 氯化铈对铝合金铬酸盐转化膜防护性能的影响
 4
 AA5052铝合金表面化学镀锡及其耐蚀性
 3
 LF21铝合金稀土转化膜的开裂及其钼酸盐后处理
 3
 改性环氧树脂无铬达克罗涂层的制备及其性能
 3
 高强度耐腐蚀铝合金的研究进展
 3
 快速凝固铜锡合金的腐蚀性能
 3
 铝合金表面微弧氧化陶瓷层的耐腐蚀性能
 3
 铝合金海水缓蚀剂研究进展
 3
 镍离子掺杂聚苯胺膜的电化学制备及其耐蚀性能
 3
 热镀锌钢板表面硅烷膜的制备工艺与耐蚀性能
 3
 热镀锌钢表面硅烷膜耐蚀性能的初步研究
 3
 热镀锌钢表面铈盐与硅烷处理后的耐蚀性能
 3
 三种镍基合金化学镀镀层的耐蚀性能
 3
 铈盐掺杂GPTMS/TEOS硅烷杂化膜腐蚀电化学行为随时间的变化
 3
 铈盐封孔对6061铝合金阳极氧化膜耐蚀性的影响
 3
 四种常用管线钢在满洲里土壤模拟溶液中的腐蚀行为
 3
 稀土硝酸盐促进的铝合金锌系磷化成膜过程
 3
 氧化钇对6061铝合金磷化膜性能的影响
 3
 一种低铬达克罗涂层的制备工艺及性能
 3