3A12、5052、6063铝合金在沿海大气环境中的腐蚀行为
          
Corrosion Behavior of 3A12, 5052, 6063 Aluminum Alloys in Coastal Atmosphere

摘    要
以盐雾模拟沿海大气环境,采用失重法、光学显微镜、X射线衍射仪(XRD)和电化学技术研究了3A12、5052、6063铝合金在沿海大气环境中的腐蚀规律及机理。结果表明:3种牌号铝合金的腐蚀质量损失与腐蚀时间均符合幂指数关系,具有相同的腐蚀产物和类似的腐蚀规律。腐蚀初期,在Cl-作用下3种铝合金发生点蚀,随后点蚀发展为全面腐蚀,全面腐蚀过程中腐蚀产物层增厚,随后腐蚀进一步发展,外层腐蚀产物发生脱落,剩余致密的腐蚀产物层。电化学测试结果表明,在沿海大气环境中,3种牌号铝合金的耐蚀性依次为:5052 > 6063 > 3A12。
标    签 铝合金   沿海大气环境   腐蚀机理   腐蚀产物   aluminum alloy   coastal atmosphere environment   corrosion mechanism   corrosion product  
 
Abstract
Salt spray was used to simulate the coastal atmospheric environment. The corrosion law and mechanism of 3A12, 5052, 6063 aluminum alloys in coastal atmospheric environment were studied by weight loss method, optical microscopy, X-ray diffraction (XRD) and electrochemical technique. The results show that the corrosion mass loss and corrosion time of the three grades of aluminum alloy were in a power exponential relationship, with the same corrosion products and similar corrosion laws. At the initial stage of corrosion, pitting corrosion occurred in the three kinds of aluminum alloy under the action of Cl-, and then pitting corrosion developed into general corrosion, and the corrosion product layer thickened during the overall corrosion process. And then corrosion further developed, and the outer corrosion product fell off, leaving a dense layer of corrosion products. Electrochemical test results show that the corrosion resistance order of the three grades of aluminum alloy in the coastal atmospheric environment was as follow:5052 > 6063 > 3A12.

中图分类号 TG174   DOI 10.11973/fsyfh-201907005

 
  购买该论文  中国光学期刊网论文下载说明


所属栏目 试验研究

基金项目

收稿日期 2018/12/2

修改稿日期

网络出版日期

作者单位点击查看


引用该论文: LI Yi,LI Kun,LI Lidong,SONG Hu,DU Tongliang,WANG Chuan,PAN Mingmin,LI Wenchao,JIANG Jiajun. Corrosion Behavior of 3A12, 5052, 6063 Aluminum Alloys in Coastal Atmosphere[J]. Corrosion & Protection, 2019, 40(7): 490


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】陈迪, 李成栋, 赵晓冬, 等. 铝合金在电力传输领域的研究及应用. 材料导报, 2013, 27(15):145-148.
 
【2】VERA R, DELGADO D, ROSALES B M. Effect of atmospheric pollutants on the corrosion of high power electrical conductors:Part 1. Aluminium and AA6201 alloy. Corrosion Science, 2006, 48(10):2882-2900.
 
【3】张春玲, 邵继领, 白丽英, 等. 铝合金芯电力电缆结构设计及过程控制. 机电信息, 2016(36):108-109, 111.
 
【4】HOLCOMB G R. Atmospheric corrosion of aluminum alloy 3105 in coastal environments:interim report after 15 months exposure. Office of Scientific and Technical Information (OSTI),:, 1996.
 
【5】罗来正, 肖勇, 苏艳, 等. 7050高强铝合金在我国四种典型大气环境下腐蚀行为研究. 装备环境工程, 2015, 12(4):49-53.
 
【6】杨大宁, 董凯辉, 符传福,等. 海南电网刀闸铝合金部件腐蚀失效分析. 腐蚀科学与防护技术, 2016, 28(1):82-87.
 
【7】东尚波. 铝合金5052海水介质腐蚀性研究. 天津:天津大学, 2010.
 
【8】孙飞龙, 李晓刚, 卢琳,等. 5052和6061铝合金在中国南海深海环境下的腐蚀行为研究. 金属学报, 2013, 49(10):1219-1226.
 
【9】AHMAD Z, UL-HAMID A, JAA B. The corrosion behavior of scandium alloyed Al 5052 in neutral sodium chloride solution. Corrosion Science, 2001, 43(7):1227-1243.
 
【10】云凤玲, 徐克. Cu2+和Fe3+离子对5052铝合金耐海水腐蚀性能的影响//海峡两岸材料腐蚀与防护研讨会.[出版地不详]:[出版者不详], 2010.
 
【11】张少军, 沈学宁, 欧阳丹霞. 时效处理对海洋用AA6063铝合金耐腐蚀性的影响. 舰船科学技术, 2016, 38(2):157-159.
 
【12】PRATIKNO H. Aging treatment to increase the erosion-corrosion resistance of AA6063 alloys for Marine application. Procedia Earth and Planetary Science, 2015, 14:41-46.
 
【13】叶群丽. 硅酸钠对3.5% NaCl溶液中6063铝合金缓蚀作用的研究. 重庆:重庆大学, 2012.
 
【14】陈海燕, 李霞, 张雪云, 等. 铝合金在海洋微生物SRB作用下的腐蚀行为. 中国有色金属学报, 2015, 25(4):1080-1085.
 
相关信息
   标题 相关频次
 平面接触型Cu/Al设备线夹的腐蚀
 4
 AA6061-T6铝合金表面纳米Y2O3改性硅烷膜的耐蚀性
 3
 腐蚀产物对6061铝合金海洋大气腐蚀过程的影响
 3
 氯化铈掺杂对6061铝合金表面硅烷膜性能的影响
 3
 1.4301不锈钢管线的腐蚀及修复
 2
 2124铝合金超厚板热轧过程温度场的数值模拟
 2
 2A12铝合金当量加速腐蚀试验
 2
 2A12铝合金微弧氧化陶瓷层的电化学腐蚀行为
 2
 2A14铝合金去应力热时效的作用
 2
 2A50铝合金钎焊钎料与钎剂的选择
 2
 304、316不锈钢和Inconel 617镍基合金在硝酸熔盐中的腐蚀行为
 2
 316NG不锈钢在高纯水环境中的腐蚀行为
 2
 3A21铝合金在乙二醇水溶液中的腐蚀行为
 2
 45#钢试件疲劳损伤的磁记忆检测
 2
 5083/6063不等厚铝合金双丝CMT角焊接头的组织与性能
 2
 5252H32铝合金维氏硬度试验的测量不确定度评定
 2
 6 mm厚铝合金板激光搭接焊T型接头焊缝的成形性能
 2
 6000系铝合金薄壁结构压缩断裂行为的有限元模拟
 2
 6061铝合金的动态拉伸性能及其本构模型
 2
 6061铝合金激光填丝焊接接头的组织与力学性能
 2
 6061铝合金汽车保险杠横梁的碰撞性能
 2
 6063铝合金挤压型材尺寸超差分析及模具优化设计
 2
 6063铝合金阳极氧化过程中麻点问题分析
 2
 6063铝合金中框侧面亮线原因分析
 2
 6082T6铝合金自动焊接工艺参数的选择
 2
 6N01铝合金中厚板三点弯曲变形行为的数值模拟
 2
 7050铝合金表面氧化膜厚度对其搅拌摩擦焊焊接接头性能的影响
 2
 7075/6009铝合金层状复合板材的固溶时效热处理工艺
 2
 7075-T6包铝材料电导率测试分析和处理
 2
 A6061-T6铝合金经超声表面纳米化后的显微组织和性能
 2